KOMPOSISI KIMIA
RUANG | % | Di | Cr | C | Bungbulang | Fe | Jeung | Jeung | P | Al | S |
Paduan 601 | MIN | 58 | 21 | - | - | kasaimbangan | - | - | - | - | - |
MAX | 63 | 25 | 0.1 | 1.5 | kasaimbangan | 0.5 | 1 | 0.02 | 1.7 | 0,015 |
Pasipatan fisik
dénsitas | titik lebur |
8,1 g/cm³ | 1320-1370 ℃ |
STANDAR EKSEKUTIF
produk | Standar ASTM |
Piring, lambar, strip | ASTM B168 |
pipa seamless & tube | ASTM B167 |
bar | ASTM B166 |
ngajalin | ASTM B564 |
DETAIL produk
The minimum sipat mékanis OFANAlloyat ROOMTEMPERATURE
kaayaan alloy | kakuatan regangan | kakuatan ngahasilkeun | Elongation |
Rm N/mm2 | Rp0,2 N/mm2 | A5% | |
anil | ≥550 | ≥205 | ≥30% |
CIRI produk
1. résistansi oksidasi unggulan dina suhu luhur;
2. lalawanan pohara alus pikeun carbonization;
3. lalawanan alus teuing pikeun oksidasi walirang-ngandung atmosfir;
4. sipat mékanis pohara alus dina duanana kamar jeung hawa tinggi;
5. résistansi pohara alus pikeun stress korosi cracking sipat alatan kadali eusi karbon jeung ukuran sisikian, 601 ngabogaan kakuatan narekahan ngabdi tinggi, jadi dina widang 500 ℃ luhur pamakéan dianjurkeun of 601.
aplikasi produk
1. Pallets na fixtures pikeun tutuwuhan Treatment panas;
2. Kawat strand annealing sarta tabung radiasi, kawat bolong kasét pikeun speed tinggi industri burner gas;
3. Tanghi isolasi dina reforming amonia jeung grids rojongan katalitik dina manufaktur asam nitrat;
4. komponén sistem knalpot;
5. Kamar durukan dina insinerators runtah padet;
6. Pipa ngarojong sarta bagian penanganan soot. Lamun dilaksanakeun dina ngeunaan 650 ° C pikeun période cukup lila, partikel karbon jeung fase kuarternér teu stabil bakal precipitated sarta bakal robah jadi Ni3(Nb,Ti) stabil rhombohedral fase kisi. Komponén platina sareng niobium dina matriks nikel-kromium anu dikuatkeun ku solusi padet bakal ningkatkeun sipat mékanis bahan, tapi plastisitasna bakal rada ngirangan.