Superalloy Seri
0102030405
KONPOZISYON CHIMIK
ESPAS | % | C | Kr | Co | NAN | Pou | Nan | Al | Nan | Fe | B | Sa a |
GH4049 | MIN | 0.04 | 9.50 | 14.00 | 5.00 | 4.50 | 0.20 | 3.70 | 1.40 | - | - | - |
MAX | 0 | 11.0 | 16.00 | 6.00 | 5.50 | 0.50 | 4.40 | 1.90 | 1.50 | 0.025 | 0.020 | |
% | 0.10 | Epi | S | P | Avèk | Pb | Avèk yon | Sn | Sb | Kòm | Nan | |
MIN | - | - | - | - | - | - | - | - | - | - | balans | |
MAX | 0.50 | 0.50 | 0.010 | 0.1 | 0.07 | 0.001 | 0.0001 | 0.0012 | 0.0025 | 0.0025 | balans |
Pwopriyete Fizik
dansite | Ranje tanperati k ap fonn |
p = 8.44g/cm | 1320-1390 ℃ |
Karakteristik pwodwi
GH4049 se yon alyaj Ni-Co-Cr ki baze sou presipitasyon redi deformation tanperati ki wo ak yon tanperati sèvis ki mwens pase 950 ℃. Alyaj la gen bon rezistans oksidasyon anba 1000 ℃ ak gwo fòs tanperati ki wo anba 950 ℃. Li apwopriye pou pwodiksyon turbine gaz lam k ap travay ak tanperati opere nan 850 ℃ ~ 950 ℃. Pwodwi prensipal yo gen ladan cho woule ak fòje ba, ak mouri fòje lam turbine. Konpare ak alyaj nikèl ki baze sou aplikasyon ki sanble, plastisit cho travay alyaj la se pòv, men apre refonn elektwoslag oswa refonn vakyòm arc, plastisit pwosesis li yo ka amelyore, ak severite enpak la nan 1000 ℃ -1170 ℃ ogmante pa 1 ~ 3 fwa.
Aplikasyon pwodwi
Alyaj la te itilize nan envantè de lam turbine motè avyon ak lòt konpozan chaj-pote wo-tanperati. Apre yon peryòd tan nan fabrikasyon ak aplikasyon, li te vin youn nan materyèl yo feyaj ki pi lajman itilize.