Usoro Alloy na-eguzogide corrosion
0102030405
NKWUKWU kemikal
Oghere | % | Fe | C | Na | Mn | P | S | Cr | Ya na | Maka | Co | Al | N'ime |
ALOY N6059 | MIN | - | - | - | - | - | - | 22 | - | 15 | - | 0.1 | itule |
MAX | 1.5 | 0.01 | 0.1 | 0.5 | 0.015 | 0.01 | 24 | 0.5 | 16.5 | 0.3 | 0.4 | itule |
Njirimara anụ ahụ
Ụdị ihe | Nha/mm | Ike/Mpa | Mgbatị A5% | ||
σb | σ1.0 | σ2.0 | |||
Mpempe akwụkwọ, efere oyi kpọnwụrụ akpọnwụ, mmanya na-ekpo ọkụ | 0.5-6.4 | ≥690 | ≥380 | ≥340 | ≥40 |
5.0-30 | ≥690 | ≥380 | ≥340 | ≥40 | |
≤100 | ≥690 | ≥380 | ≥340 | ≥40 | |
Ọkọlọtọ EXECUTIVE
Ngwaahịa | ASTM Standard |
ọkpọkọ&tube enweghị nkebi | B622 |
Ọkụ&tube agbadoro | B619/B626 |
Efere | B575 |
Ogwe, waya | B574 |
Mwepu | B575 |
Na-akpụ akpụ | B564 |
Njirimara ngwaahịa
Nguzogide dị oke mma maka ikpochapụ corrosion, crevice corrosion na chloride na-akpata nrụgide corrosion crack; iguzogide corrosion megide inorganic acid, dị ka nitric acid, phosphoric acid, sulfuric acid, na hydrochloric acid, karịsịa na ngwakọta nke sulfuric acid na hydrochloric acid; iguzogide corrosion nke ihe ngwọta agwakọta inorganic acid dị iche iche; ezigbo nguzogide corrosion na ngwọta hydrochloric acid dị iche iche ruo 40 ℃ (104 Celsius F); ezi workability na weldability, ọ dịghị post-weld cracking uche; asambodo nrụpụta maka ụgbọ mmiri nrụgide nwere okpomọkụ sitere na 196 ruo 450 ℃. Ọ nwere ezi workability na weldability, ọ dịghị susceptibility ka post-weld cracking; a kwadoro ya maka imepụta arịa nrụgide na okpomọkụ sitere na -196 ruo 450 ℃.
Ngwa ngwaahịa
N'ihe banyere iji acid chloride catalysts, digesters na bleaching equipment in the pulp and paper industry, scrubbers, reheaters, throttle valves, mmiri mmiri Fans na agitators na FGD na IG usoro, ngwá na components na-arụ ọrụ na acid gas ikuku, reactors maka acetic acid na acetic anhydride ngwaahịa, sulfuric acid condens.