Superalloy Series
0102030405
CHEMICAL COMPOSITIONE
TRACTUS | % | C | Cr | Co | IN' | For | In | Al | Of | Fe | B | Hoc |
GH4049 | MIN | 0.04 | 9.50 | 14.00 | 5.00 | 4.50 | 0.20 | 3.70 | 1.40 | - | - | - |
MAX | 0 | 11.0 | 16.00 | 6.00 | 5.50 | 0.50 | 4.40 | 1.90 | 1.50 | 0.024 | 0.018 | |
% | 0.10 | And | S | P | cum | Pb | Cum a* | Sn | Sb* | As | In | |
MIN | - | - | - | - | - | - | - | - | - | - | statera | |
MAX | 0.50 | 0.50 | 0.011 | 0.1 | 0.07 | 0.001 | 0.0001 | 0.0012 | 0.0025 | 0.0025 | statera |
Corporalia Properties
density | Liquefaciens temperatus range |
p=8.44g/cm | 1320-1390℃ |
Product pluma
GH4049 est Ni-Co-Cr substructio praecipitationis obdurationis deformationis caliditas mixturae cum servitio temperaturae minoris quam 950℃. Admisceri bonam oxidationis resistentiam habet sub 1000℃ et caliditas calidissimae vires sub 950℃. Opportunus est productioni gasi turbine laminarum laborantium cum temperie operante 850℃~950℃. Summa productorum includunt calidum revolutum et fictum vectem, et moriuntur in ensem turbine laminae. Comparatus cum nickel-substructio admixtionum similium applicationum, mixturae calidae plasticitatis laborantis pauper est, sed post electroslagum remotionem vel arcum vacuum dissolutum, eius processus plasticitas emendari potest, et impetus durities 1000℃-1170 augetur per 1~3 tempora.
Product application
stannum adhibitum est in fabricando machinae machinae in scapulis cinematographicis et aliis elementis summus temperatus onere ferens. Post longum tempus fabricandi et applicationis, una ex late usa materia foliorum facta est.