Superalloy Series
0102030405
COMPOSITION CHEMIKA
toerana | % | In | Cr | Fe | HO AN'NY | Nb | mpiara | C | Mn | SY | S | amin'ny | Al | nY | t | amin ' |
GH4169 | MIN | 50 | 17 | Mila mahay mandanjalanja | 2.8 | 4.75 | - | - | - | - | - | - | 0.2 | 0.65 | - | - |
MAX | 55 | 21 | Mila mahay mandanjalanja | 3.3 | 5.5 | 1 | 0.08 | 0.35 | 0.35 | 0.015 | 0.3 | 0.8 | 1.15 | 0.015 | 0.06 |
Toetra ara-batana
hakitroky | Fanjakana Alloy | faharetana amin'ny sintona | manome hery | Elongation | Elongation |
| Rm N/mm2 | Rp0,2 N/mm2 | A5% | HB | |
8.24g/cm | Fitsaboana vahaolana mafy | ≥965 | ≥550 | ≥30% | ≤363 |
Vahaolana mafy + fahanterana | ≥1275 | ≥1034 | ≥12% | ≥331 |
STANDARD EXECUTIVE
VOKATRA | ASTM fenitra | ASME standard |
Taratasy, takelaka, Strip | B670 | SB670 |
Sodina & fantsona tsy misy seam | B983 | - |
welded Pipe&tube | - | - |
Bar, mofomamy | B637 | SB637 |
manorina | B670 | SB670 |
Wire | - | - |
FEATURE vokatra
1. mora machinability. 2. tanjaka avo lenta, tanjaky ny harerahana, tanjaky ny creep ary tanjaky ny fracture amin'ny 700 ° C. 3. avo oxidation fanoherana amin'ny 1000 ° C. 4. firafitry ny simika miorina amin'ny mari-pana ambany. 5. weldability tsara.
Fampiharana vokatra
Noho ny tanjaky ny mari-pana ambony sy ny fanoherana ny harafesina tsara amin'ny 700 ℃, ny fanodinana mora 718 dia azo ampiasaina betsaka amin'ny toe-javatra sarotra be.