Serje Superalloy
0102030405
GĦAMLA KIMIKA
SPAZJU | % | Ċ | U | Mn | P | S | Cr | Fil | Għal | Bil | Al | Ta | Fe | Co | B | Zr |
GH4738 | MIN | 0.03 | - | - | - | - | 18.0 | bilanċ | 3.5 | - | 1.20 | 2.75 | - | 12.0 | 0.003 | 0.02 |
MAX | 0.10 | 0.15 | 0.10 | 0.015 | 0.015 | 21.0 | bilanċ | 5.0 | 0.10 | 1.60 | 3.25 | 2.00 | 15.0 | 0.01 | 0.08 |
Proprjetajiet Fiżiċi
densità | Firxa tat-temperatura tat-tidwib |
p=8.22g/ċm | 1330-1360℃ |
STANDARD EŻEKUTTIV
Standard Nru & Varjetà | stat tal-kampjun | Ħxuna tal-pjanċa 8/mm | Proprjetajiet tat-tensjoni | 730°C Durabilità | Ebusija tat-temperatura tal-kamra | |||||
θ/℃ | Saħħa tat-tensjoni | saħħa ta 'rendiment | A5% | σ/MPa | Ħin/h | A% | ||||
QJ/DT01.63026 | Stat tal-provvista | ≤0.50 | 20 | ≥1170 | ≥760 | ≥15 |
| - | L | (34 sa 44) HRC jew ekwivalenti |
540 | ≥1000 | ≥690 | ≥13 |
| - |
|
| |||
> 0.50 | 20 | ≥1205 | ≥795 | ≥20 | - |
| - | (34 sa 44) HRC jew ekwivalenti | ||
540 | ≥1035 | ≥725 | ≥15 |
|
| - |
| |||
> 0.40 ~ 0.50 |
|
|
|
| 430 | ≥23 | ≥4 |
| ||
> 0.50 |
|
|
|
| 430 | ≥23 | ≥4 | |||
KARATTERISTIKA TAL-Prodott
GH738 huwa liga ta 'temperatura għolja bbażata fuq in-nikil imwebbes minn preċipitazzjoni tal-fażi γ', b'reżistenza tajba għall-korrużjoni tal-gass, qawwa għolja ta' rendiment u proprjetajiet ta 'għeja, plastikità tajba tal-proċess u organizzazzjoni stabbli. Użat ħafna fil-partijiet li jduru tal-magni tal-inġenji tal-ajru, l-użu tat-temperatura mhuwiex ogħla minn 815 ℃. Jista 'jipproduċi pjanċi rrumblati fil-kesħa u rrumblati bis-sħana, pajpijiet, strixxi, wajers, forġa, kkastjar u qfieli.
Applikazzjoni tal-prodott
Magni tal-ajruplani, turbini tal-gass tal-magni, xfafar tat-turbini u diski tat-turbini u partijiet oħra li jduru.