Korroziyaga chidamli qotishma seriyasi
0102030405
Qotishma B-3/N10675
KIMYOVIY TARKIBI
SPACE | % | In | Cr | uchun | Fe | IN | Co | C | Bilan | Al | Mn | Of | Va | Nb | In | Yurish | P | Zr | S | By+You |
qotishma B-3 | MIN | ≥65 | 1 | 27 | 1 | _ | _ | _ | _ | _ | _ | _ | _ | _ | _ | _ | _ | _ | _ | 94 |
MAX | 3 | 32 | 3 | 3 | 3 | 0,01 | 0.2 | 0,5 | 3 | 0.2 | 0.1 | 0.2 | 0.2 | 0.2 | 0,03 | 0,03 | 0,01 | 98 |
Jismoniy xususiyatlar
zichligi | erish nuqtasi | Qotishma holati | mustahkamlik chegarasi | hosil kuchi | Tanaffus paytida cho'zilish |
9,24 g/sm³ | 1370-1418 ℃ | A | Rm N/mm2 | Rp0,2 N/mm2 | A5% |
≥760 | ≥350 | ≥40 |
IJROCHI STANDART
Mahsulot | ASTM standarti |
bar | ASTM B335 |
Varaq/tasma | ASTM B333 |
choksiz quvur va quvur | ASTM B622 |
payvandlangan quvur va quvur | ASTM B619 |
payvandlangan quvur va quvur | ASTM B626 |
Flanjli valf materiali | ASTM B564 |
zarb qilish | ASTM B564 |
Mahsulot Xususiyati
1. B-3 qotishmasi nikel qotishmalari oilasining yangi a'zosi bo'lib, u har qanday harorat va konsentratsiyada xlorid kislotaga mukammal korroziyaga chidamliligiga ega, shuningdek, sulfat kislota, sirka kislotasi, formik kislota, fosfor kislotasi va boshqa oksidlovchi bo'lmagan vositalarga yaxshi korroziyaga chidamli.
2. Kimyoviy tarkibini sozlash tufayli uning termal barqarorligi dastlabki B-2 qotishmasi bilan solishtirganda ancha yaxshilandi. B-3 qotishmasi payvandlashning issiqlik ta'sir zonasida chuqur korroziyaga, kuchlanish korroziyasiga, to'sar korroziyasiga va korroziyaga yuqori qarshilikka ega.
ilova
B-3 qotishmasi avvalgi B-2 qotishmasining barcha ilovalarida ishlatilishi mumkin. B-2 qotishmasi singari, B-3 uch valentli temir va ikki valentli mis tuzlari mavjud bo'lgan muhitda foydalanish uchun tavsiya etilmaydi, chunki bu tuzlar tezda korroziyaga olib kelishi mumkin. Xlorid kislota temir va mis bilan aloqa qilganda ular bilan kimyoviy reaksiyaga kirishib, uch valentli temir va ikki valentli mis tuzlarini hosil qiladi.