Superalloy Series
01
CHEMICAL COMPOSITIONE
Eraum Alloy | % | C | And | Mn | Cr | N | P | S | Al | B | Fe | Tu | Co | IN' | Hoc | For |
GH99 | MIN | - | - | - | 17 | pulvinar | - | - | 1.7 | - | - | 1 | 5 | 5 | - | 3.5 |
MAX | 0.08 | 0.5 | 0.4 | 20 | pulvinar | 0.014 | 0.014 | 2.4 | 0.005 | 2 | 1.5 | 8 | 7 | 0.02 | 4.5 |
PHYSICA POTESTAS
Density | punctum liquescens |
8.47g/cm2 | 1345℃-1390℃ |
Materia Technical Signa
GB/T 14992 Classificationis et gradus summus temperaturae mixtionum et compositionum intermetallicarum pro materiarum temperaturarum summus
GJB 1952A Specificatio ad schedam frigidam involutum caliditatis mixturae ad usum aviationis
HB/Z 140 Calor curatio processus summus temperatus admixtis applicationibus aerospace
Feature
GH99 est Ni-Cr fundatum praecipitatio obdurationis deformationis stannum caliditatis, quod infra CM°C diu adhiberi potest, et breve tempus maximum temperamentum ad 1000°C attingere potest. GH99 mixtura roboratur addendo chromium, cobaltum, tungsten et molybdaenum ad solidam solutionem corroborandam, aluminium et titanium ad incrementa senescentem corroborandum, et boron, cerium et magnesium ad purgandum et confirmandum limites frumenti. GH99 mixtura altiorem vim scelerisque, stabilis dispositionem et satis frigidum et calidam machinationem formans et glutinosa proprietates habet. GH99 mixtura altam vim thermarum, organicam stabilitatem habet, et processus satisfactorius calidus et frigidus processus faciendi et glutinous effectus est. GH99 apta est ad machinationem aero-machinam gazophylacium combustionis fomitem et gazophylacium combustionis aliasque partes altae temperaturae iunctas. Praecipua producta GH99 sunt vectes, laminae, filis et malleationes calidae involutae. Cum admixto per magnam structuram laminae fabricatam, protinus post solidam solutionem Curatio sine curatione senescente adhiberi potest. stannum non inventum est post diuturnum tempus 700℃~950 senescentem augmenta nociva habere.