Superalloy Series
0102030405
CHEMICAL COMPOSITIONE
TRACTUS | % | C | And | Mn | Cr | In | P | S | Al | B | Fe | Of | Co | IN' | Hoc | For | Mg |
GH99 | MIN | - | - | - | 17.0 | statera | - | - | 1.70 | - | - | 1.00 | 5.00 | 5.00 | - | 3.50 | - |
MAX | 0.08 | 0.50 | 0.40 | 20.0 | statera | 0.014 | 0.014 | 2.40 | 0.005 | 2.00 | 1.50 | 8.00 | 7.00 | 0.02 | 4.50 | 0.01 |
Corporalia Properties
density | liquescens punctum |
8.47g/cm3 | 1345-1390℃ |
Product pluma
GH99 est Ni-Cr fundatum praecipitationis obdurationis deformitatis mixturae caliditas, quae ad longum tempus infra DCCCC°C adhiberi potest, et maximum breve tempus servitutis temperaturae 1000°C attingere potest. GH99 mixtura corroboratur adiectione chromii, cobalti, tungi et molybdaeni ad solidam solutionem solidandam, addito aluminio et titanio ad incrementa senescentes formandos, addita boroni, cerii et magnesii ad limites frumenti purgandos et confirmandos. GH99 mixtura altam vim thermarum, dispositionem stabilem habet, et machinationem calidam et frigidam sufficientem habet processus faciendi et glutino fabricandi. GH99 apta gazophylacia combustionis aero-machinae ac fomitibus combustionis cubicula et alia temperatura iuncta partium structurarum. Praecipua producta GH99 sunt vectes, laminae, filis et malleationes involutae calidae. Cum admixto per magnam structuram laminae fabricatam, protinus post solidam solutionem Curatio sine curatione senescente adhiberi potest. Admisceri per 700 ℃ ~ 950 longi temporis senescentis incrementa noxia non invenit.
Product application
Mixtura adhibita est in productione processus machinalis aero-conficii aptabilis, vis dolii et aliarum partium; talea convoluta adhibita in fabricando laminarum aero-enginerum compressorum; bar fictus adhibitus est in fabricandis magnis turbines gasorum navalium et cruise missilium partium structurarum.