CHEMICAL COMPOSITIONE
TRACTUS | % | C | And | Mn | P | S | In | Cr | cum | Nb | Al |
17-4PH | MIN | - | - | - | - | - | 3.0 | 15.0 | 3.0 | 0.15 | - |
MAX | 0.07 | 1.0 | 1.0 | 0.04 | 0.03 | 5.0 | 17.5 | 5.0 | 0.45 | - | |
17-7PH | MIN | - | - | - | - | - | 6.5 | 16.0 | - | - | 0.75 |
MAX | 0.09 | 1.0 | 1.0 | 0.04 | 0.03 | 7.75 | 18.0 | - | - | 1.5 |
Corporalia Properties
Exemplar | 17-4PH | 17-7PH |
Density | 7.85g/cm3 | 7.85g/cm3 |
punctum liquescens | 1404-1440℃ | 1404-1440℃ |
Product pluma
17-4PH Chromium-Nickel-aerarium praecipitatio martensitica indurata ferro immaculata. Hic gradus chalybis immaculati notatur magna vi, duritie et corrosione resistendi. Proprietates mechanicae meliorantur calore Curationis et virium compressivorum usque ad 1100-1300 MPa (160-190 ksi) effici posse. Hic gradus temperaturis supra CCC°C adhiberi non potest (572°F) vel in calidissimis temperaturis. Repugnantiam atmosphaericam et dilutam acida vel salia bene habet, eiusque resistentia corrosio cum 304 .
17-7PH est praecipitatio austenitico-martensitica durities incorrupta chalybis innixa, ex 18-8CrNi evoluta, quae mutatio Phase intemeratae chalybe incorrupta nota est. 17-7PH chalybs immaculatus instabilis est austenitica ordinatio post solidam solutionem curationis, cum bona plastica duritiem et machinabilitatem, post temperantiam, ut austenite praecipitatio carbidum post mutationem compositionis, et deinde per processum transmutationis martensiticum, pleraque ordinatio transmutetur in processum temperaturae carbonis humilem cum bona duritia. Post temperaturam, austenite praecipitatio carbida compositionis mutatur, et deinde per processum transmutationis martensiticae, maxime organisationis martensitae cum bono duritie temperato in vilem carbonis temperatum mutatur, et bonas proprietates mechanicas in temperatura media habet. 17-7PH resistentia corrosio melior est ferro incorrupta quam generalis martensitica.