Serje ta 'liga reżistenti għall-korrużjoni
0102030405
Liga B-3/N10675
GĦAMLA KIMIKA
SPAZJU | % | Fil | Cr | Għal | Fe | IN | Co | Ċ | Bil | Al | Mn | Ta | U | Nb | Fil | Niffaċċjaw | P | Zr | S | Minn+Tek |
LIGA B-3 | MIN | ≥65 | 1 | 27 | 1 | _ | _ | _ | _ | _ | _ | _ | _ | _ | _ | _ | _ | _ | _ | 94 |
MAX | 3 | 32 | 3 | 3 | 3 | 0.01 | 0.2 | 0.5 | 3 | 0.2 | 0.1 | 0.2 | 0.2 | 0.2 | 0.03 | 0.03 | 0.01 | 98 |
Proprjetajiet Fiżiċi
densità | punt tat-tidwib | Stat tal-liga | saħħa tat-tensjoni | saħħa ta 'rendiment | Titwil fil-waqfa |
9.24g/cm³ | 1370-1418℃ | A | Rm N/mm2 | Rp0.2 N/mm2 | A5% |
≥760 | ≥350 | ≥40 |
STANDARD EŻEKUTTIV
Prodott | Standard ASTM |
bar | ASTM B335 |
Folja/strixxa | ASTM B333 |
pajp u tubu mingħajr saldatura | ASTM B622 |
pajp u tubu wweldjati | ASTM B619 |
pajp u tubu wweldjati | ASTM B626 |
Materjal tal-Valv tal-Flanġ | ASTM B564 |
forġa | ASTM B564 |
KARATTERISTIKA TAL-Prodott
1. Liga B-3 hija membru ġdid tal-familja tal-liga tan-nikil, għandha reżistenza għall-korrużjoni eċċellenti għall-aċidu idrokloriku fi kwalunkwe temperatura u konċentrazzjoni, kif ukoll reżistenza tajba għall-korrużjoni għall-aċidu sulfuriku, aċidu aċetiku, aċidu formiku, aċidu fosforiku, u midja oħra mhux ossidanti.
2. Minħabba l-aġġustament tal-kompożizzjoni kimika tiegħu, l-istabbiltà termali tagħha tjiebet ħafna meta mqabbla mal-liga B-2 oriġinali. Liga B-3 għandha reżistenza għolja għall-korrużjoni tal-pitting, korrużjoni tal-istress, korrużjoni tal-qtugħ u korrużjoni fiż-żona tal-iwweldjar affettwata bis-sħana.
applikazzjoni
Liga B-3 tista 'tintuża fl-applikazzjonijiet kollha tal-liga B-2 preċedenti. Bħal liga B-2, B-3 mhux rakkomandat għall-użu f'ambjenti fejn ħadid trivalenti u melħ tar-ram divalenti huma preżenti, peress li dawn l-imluħa jistgħu malajr jikkawżaw ħsara mill-korrużjoni. Meta l-aċidu idrokloriku jiġi f'kuntatt mal-ħadid u r-ram, jirreaġixxi kimikament magħhom biex jifforma ħadid trivalenti u melħ tar-ram divalenti.