Superalloy Series
01
KOMPOSISI KIMIA
Eraum Alloy | % | C | Cr | Di | Co | Pikeun | AI | OF | B | Fe | Zr | Bungbulang | Jeung | P | S |
GH141 | MIN | 0.06 | 180 | bantal | 100 | 90 | 1.4 | 3 | 0.003 | - | - | - | - | - | - |
MAX | 0.12 | 20 | bantal | 120 | 10.5 | 1.8 | 3.5 | 0.01 | 5 | 0.07 | 0.5 | 0.5 | 0,015 | 0,015 |
SIFAT FISIK
Kapadetan | Titik lebur |
ρ = 8,27g/cm3 | 1316-1371 ℃ |
STANDAR EKSEKUTIF
Q / 3B 4060-1992 GH141 alloy Bar jeung strips
Q / 3B 4063-1992 GH141 alloy tiis digulung strip
Q / 5B 4027-1992 GH141 cakram alloy, cingcin, sareng bagian annular
Q / 6S 1033-1992 GH141 bar alloy pikeun fasteners suhu luhur
GB / T 14992 Klasifikasi sareng sasmita bahan suhu luhur sapertos alloy suhu sareng sanyawa logam
HB / Z 140 Proses Perlakuan Panas tina alloy suhu luhur pikeun aplikasi aerospace
GJB 2456 Spésifikasi pikeun bar rolled panas tina GH4141 alloy suhu luhur pikeun pamakéan aerospace
Fitur produk
GH141 nyaéta présipitasi hardening deformasi dumasar-nikel alloy suhu luhur, dina rentang 650 ~ 950 ℃, ngabogaan tensile tinggi jeung kakuatan ngabdi lila-langgeng jeung résistansi oksidasi alus; alatan kandungan luhur aluminium, titanium jeung molybdenum dina alloy nu, hese tuang ingot billet, tapi deformasi bahan ngabogaan plasticity hadé, dina kaayaan annealed tiasa tiis ngabentuk, ogé bisa dilas, bagian dilas anu rawan galur sepuh panas retakan Treatment. bagian dilas anu rentan ka galur retakan sepuh salila perlakuan panas. The alloy sadia dina lambar, strip, kawat, cakram, cingcin, forgings, rod, sarta castings precision.