Superalloy Seri
01
KONPOZISYON CHIMIK
Eraum alyaj | % | C | Kr | Nan | Co | Pou | AI | OF | B | Fe | Zr | Mn | Epi | P | S |
GH141 | MIN | 0.06 | 180 | kousen | 100 | 90 | 1.4 | 3 | 0.003 | - | - | - | - | - | - |
MAX | 0.12 | 20 | kousen | 120 | 10.5 | 1.8 | 3.5 | 0.01 | 5 | 0.07 | 0.5 | 0.5 | 0.015 | 0.015 |
PWOPRIYETE FIZIK
Dansite | Pwen k ap fonn |
ρ=8.27g/cm3 | 1316-1371 ℃ |
Egzekitif STANDARD
Q/3B 4060-1992 GH141 Alloy Bars and Strips
Q/3B 4063-1992 GH141 alyaj frèt woule teren
Q/5B 4027-1992 GH141 disk alyaj, bag, ak pati annulaire
Q/6S 1033-1992 GH141 ba alyaj pou fixation tanperati ki wo
GB/T 14992 Klasifikasyon ak klas materyèl ki wo tanperati tankou alyaj tanperati ak konpoze metal
HB/Z 140 Pwosesis Tretman Chalè nan alyaj tanperati ki wo pou aplikasyon ayewospasyal
GJB 2456 Spesifikasyon pou ba woule cho nan alyaj tanperati ki wo GH4141 pou itilize ayewospasyal.
Karakteristik pwodwi
GH141 se presipitasyon redi nikèl ki baze sou deformation nan alyaj tanperati ki wo, nan seri a nan 650 ~ 950 ℃, gen yon gwo rupture ak fòs ki dire lontan ak bon rezistans oksidasyon; akòz kontni an segondè nan aliminyòm, Titàn ak molybdène nan alyaj la, li difisil jete billet ingot, men deformation nan materyèl la gen yon plastisit pi bon, nan eta a annealed ka frèt fòme, kapab tou soude, pati soude yo se tendans souch aje chalè Tretman fant. Pati soude yo sansib a souch aje fant pandan Tretman chalè. Alyaj yo disponib nan fèy, teren, fil, disk, bag, forgings, baton, ak depoze presizyon.